Fast calorimetric scanning of micro-sized SnAgCu single droplet at a high cooling rate

查看全文 作　　者：GAO [1]YuLai;ZOU [1]ChangDong;YANG [1]Bin;ZHAI [1]QiJie

机构地区：[1]School of Materials Science and Engineering,Shanghai University,Shanghai 200072,China

出　　处：《Science China(Technological Sciences)》索引2009年第52卷第6期,共5页

基　　金：Supported by the Robert Bosch Foundation(Grant No.32.5.8003.0025.0/MA01);the National Natural Science Foundation of China(Grant No.50571057);the National High-Tech Research and Development Program of China('863' Project)(Grant No. 2006AA03Z339);the Shanghai Rising-Star Program(Grant No.06QA14020) 摘　　要：The undercooling of the single micro-sized droplet of Sn-3.0Ag-0.5Cu(wt%)alloy has been studied via the newly developed fast calorimetric scanning technique,by which the fast heating and cooling treatment for a single droplet can be realized,with the maximum heating or cooling rate being 1×104K/s.Owing to the nearly spherical shape of the single droplet upon heating and cooling and the resul-tant geometric stability,the influence of the droplet size on the solidification process could be elimi-nated.As a result,the puzzled issue on how to separate the mutual effects of droplet size and cooling rate in the field of rapid solidification has been primarily solved,making it possible to study separately the effect of droplet size and cooling rate.Meanwhile,the in-situ observation on deep undercooling could be actualized in this condition,differing from that obtained only by theoretical calculation.The results showed that the undercooling was increased with the increasing cooling rate,and the maximum in-situ measured undercooling reached 116.9K.The undercooling of the single droplet,however,was increased abruptly when cooled at the rate of 2×103K/s.The undercooling increased slightly as the cooling rate was increased continuously to 1×104K/s,implying the infeasibility for gaining large undercooling only by increasing the cooling rate. 关键词：fast SCANNING CALORIMETRY single droplet large cooling rate UNDERCOOLING

相关文献

参考文献（21）
引证文献（2）
耦合文献（6）

参考文献(21)

引证文献(2)

耦合文献(6)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Fast calorimetric scanning of micro-sized SnAgCu single droplet at a high cooling rate

参考文献(21)

引证文献(2)

耦合文献(6)

用户提示