Characterization of Electroless Ni-P Deposits on Surface of AZ91D Magnesium Alloy

查看全文 作　　者：Li [1]Jiansan;Guo Yanting;Liu Junquan 高影响力作者 机构地区：[1]S China Univ Technol, Sch Mech & Automot Engn, Inst Corros Control & Surface Engn, Guangzhou 510640, Guangdong, Peoples R China高影响力机构 出　　处：《稀有金属材料与工程》索引2012年第41卷第S1期,共4页高影响力期刊 基　　金：Guangdong Provincial Department of Science and Technology(2008B090500096) 摘　　要：Characterization of electroless nickel deposits on magnesium alloys was investigated by X-ray diffraction(XRD),scanning electron microscope(SEM),energy dispersive spectrometer(EDS)and electrochemical potentiodynamic polarization analysis.The result of XRD showed that the electroless nickel deposits on magnesium alloys were composed mostly of amorphous Ni-P and partially of microcrystalline nickel.The phosphorus content in the Ni-P deposits was 10.8%by the calculation of EDS.SEM micrographs showed that morphology of electroless nickel deposits on magnesium alloys was a typical cellular structure,and the growth of cellular structure was influenced by surface condition of substrate.Zinc layer between substrate and electroless nickel deposits was not found by the results of SEM and EDS,which indicated that the zinc layer on the surface of magnesium alloy was very thin,and the zinc would dissolved while being immersed in electroless nickel plating solution.The thin zinc layer was almost dissolved completely before Ni-P plating.The result of electrochemical potentiodynamic polarization analysis showed that the corrosion potential Ecorr of electroless nickel deposits in 3.5%NaCl solution was about-0.53 V,which was 1 V higher than that of magnesium alloys substrate.And corrosion current density of Ni-P deposits in 3.5%NaCl solution was much smaller than that of magnesium alloys substrate at the same potential value,which indicated that corrosion resistance of electroless Ni-P deposits was excellent.Discoloration time of concentrated nitric acid test for electroless nickel deposits on magnesium alloys was 445 s,which also indicated excellent corrosion resistance. 关 键 词：MAGNESIUM alloy ELECTROLESS NICKEL PLATING corrosion resistance structure
相关文献

参考文献(10)

引证文献(3)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费