SiC fiber with low electrical resistivity and oxygen content

查看全文 作　　者：WANG DeYin,MAO XianHe,SONG YongCai & WANG YingDe State Key Lab of Novel Ceramic Fibers and Composites,National University of Defense Technology,Changsha 410073,China

出　　处：《Science China(Technological Sciences)》索引2010年第53卷第4期,共5页

摘　　要：A new SiC fiber was prepared by the pyrolysis of polycarbosilane(PCS) fiber cured with unsaturated hydrocarbons.The fiber,with oxygen content of 4-6 wt%,offers high tensile strength of 2.5-2.8 GPa.The electrical resistivity of the fiber is only about 0.5 Ω·cm,much lower than general SiC fiber obtained from traditional air curing process.Degradation of mechanical property in argon and air at high temperature is retarded by 200-300℃ with respect to the Nicalon NL-202 fiber.The low electrical resistivity of the fiber exhibits excellent thermal stability,it almost remains 0.4-0.8 Ω·cm after thermal exposure test from the room temperature to 1600℃ in argon.The low electrical resistivity mainly attribute to an excess carbon layer which is about 50 nm in the circular outer part. 关键词：polycarbonsilane SIC FIBER electrical RESISTIVITY EXCESS CARBON LAYER

相关文献

参考文献（18）
引证文献（3）
耦合文献（11）

参考文献(18)

引证文献(3)

耦合文献(11)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

SiC fiber with low electrical resistivity and oxygen content

参考文献(18)

引证文献(3)

耦合文献(11)

用户提示