Microstructure of fibrils separated from polyacrylonitrile fibers by ultrasonic etching

查看全文 作　　者：WANG QiFen,WANG ChengGuo,YU MeiJie,MA Jie,HU XiuYing & ZHU Bo Carbon Fiber Engineering Research Center,Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education),Shandong University,Jinan 250061,China

出　　处：《Science China(Technological Sciences)》索引2010年第53卷第6期,共6页

基　　金：supported by the National Natural Science Foundation of China (Grant No.50673052);the Major State Basic Research Development Program of China (973 Program) (Grant No.2006CB605314);the Provincial Natural Science Foundation of Shandong Province (Grant No.Z2008F02) 摘　　要：Polyacrylonitrile (PAN) fiber is an important precursor fiber for high performance carbon fiber.The properties of the final carbon fiber depend strongly on the nature of the PAN fibers.The PAN fibrils were separated successfully from fibers by ultrasonic etching and were systematically investigated by field emission scanning electron microscopy (FESEM) and high resolution transmission electron microscopy (HRTEM).It is found that in certain ultrasonic etching conditions (at 75±2oC for 6 h with a frequency of 40 kHz) the PAN fibers are dissolved in the 95 wt.% aqueous dimethylsulphoxide (DMSO) solution;the fibrils consisting of numerous periodic lamellae with thickness of 30-45 nm and perpendicular to the fiber axis are separated in the 90 wt.% aqueous DMSO solution;and the fibrils with smooth surface exfoliated from the PAN fibers are obtained in the 70-90 wt.% aqueous DMSO solutions.Inner periodical structure of fibrils was observed in HRTEM,which indicates that there are different densities and two phases in fibrils.The PAN fibers are dissolved layer by layer with increasing ultrasonic etching time.The fiber surface experiences ultrasonic cleaning,selective etching,excessive etching and dissolution,and then the sublayer experiences the same process.There are numerous periodic lamellae in fibrils of nascent fibers.This means that the fibrils with lamellae are formed by orientation and crystallization in shearing field of spinning pipe and drawing stress field of coagulation bath. 关键词：carbon fibers PAN fibers FIBRILS MICROSTRUCTURE

相关文献

参考文献（15）
引证文献（4）
耦合文献（59）

参考文献(15)

引证文献(4)

耦合文献(59)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Microstructure of fibrils separated from polyacrylonitrile fibers by ultrasonic etching

参考文献(15)

引证文献(4)

耦合文献(59)

用户提示