MICROSTRUCTURAL STUDY OF Fe-Cr-Al/Al COMPOSITE COATINGS DURING OXIDATION AND SULFIDATION AT 900℃

查看全文 作　　者：Z.L. Zhang D.Y. Li X.Q. [1]Dong 高影响力作者 机构地区：[1]School of Material Science and Engineering, Shenyang University of Technology, Shenyang 110023, China高影响力机构 出　　处：《Acta Metallurgica Sinica(English Letters)》索引2007年第20卷第2期,共8页高影响力期刊 摘　　要：The microstructure of a composite coating system,which was composed of an inner layer of Fe-Cr-Al and an outer layer of aluminum,was studied after it was respectively oxidized and sulfurdized at elevated temperatures. Apart from the Al2O3 scale formed on the surface,the microstructure of the composite coatings exposed at 900℃ in air for 4h was a three-layer structure. The first layer consisted of a solid solution of Cr and Fe in α aluminum and an intermetallic compound FeAl3,while the second layer was a single phase of the aluminide and the third layer still remained the same appearance as the original Fe-Cr-Al coating. The microstructural observation of the specimen tested at 850-900℃ at low oxygen pressure and high sulfur pressure for 576h revealed that the surface coatings of the specimen had transformed into a duplex structure containing an outer layer and a thicker aluminide layer beneath. X-ray diffraction results showed that the out layer was composed of Al2S3 and Al2O3 and that AlCrFe2 was the main phase composition of the aluminide layer,with a few of Al2S3 and Al2O3 accompanied. 关 键 词：Fe-Cr-Al/Al复合镀层 高温硫化 高温氧化 显微结构 电弧喷镀层
相关文献

参考文献(5)

引证文献(2)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费