Effects of the two-step ageing treatment on the microstructure and properties of 7B04 alloy pre-stretched thick plates

查看全文 作　　者：LI Zhihui XIONG Baiqing ZHANG Yong 'an ZHU Baohong WANG Feng LIU [1]Hongwei

机构地区：[1]State Key Laboratory for Fabrication and Processing of Nonferrous Metals, General Research Institute for Nonferrous Metals, Beijing 100088, China

出　　处：《Rare Metals》索引2007年第26卷第3期,共7页

基　　金：the National High-Tech Research Development Program of China (No. 2003AA331100). 摘　　要：The effects of the two-step ageing parameters (temperature and time) on the mechanical properties and electrical conductivity of 7B04 (Al-Zn-Mg-Cu) pre-stretched thick plates were studied. The results reveal that the initial T1 ageing contributes a major increase of the tensile strength, and the 0.2% proof stress value reaches 482 MPa after ageing for 7 h at 115°C. Behavioral differences in the tensile properties of the alloy after the two-step ageing treatment were less with the first-step ageing at 115°C for different time periods (7, 14, and 21 h). The effects of the second ageing parameters on the properties and microstructure of the 7B04 alloy were remarkable. TEM analysis of the samples aged at Temper I (7 h at 115°C + 12 h at 160°C) and Temper II (7 h at 115°C + 16 h at 165°C) indicates that two kinds of phases, i.e. η′ and η phases, precipitate from the matrix and efficiently improve the tensile strength of the alloy, and the grain boundary precipitates are coarse and discrete. There are obvious precipitate free zones (PFZs) along the grain boundary in the microstructure of the alloy after the two-step ageing treatment. 关键词：7B04合金老化机械性能导电率微观结构

相关文献

参考文献（18）
引证文献（26）
耦合文献（102）

参考文献(18)

引证文献(26)

耦合文献(102)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Effects of the two-step ageing treatment on the microstructure and properties of 7B04 alloy pre-stretched thick plates

参考文献(18)

引证文献(26)

耦合文献(102)

用户提示