Hot spinning of cylindrical workpieces of TA15 titanium alloy

查看全文 作　　者：XU Wenchen,SHAN Debin,YANG Guoping,CHEN Yu,LU Yan,and KANG Dachang School of Materials Science and Engineering,Harbin Institute of Technology,Harbin 150001,China

出　　处：《Rare Metals》索引2007年第26卷第S1期,共7页

摘　　要：In order to form large-diameter thin-wall cylindrical workpieces of TA15 titanium alloy,tube hot spinning experiments of the alloy were conducted on a CNC hot spinning machine.The causes of some forming defects occuring in hot spinning,such as crack,pileup,bulge and corrugation,were analyzed and the corresponding measures were put forward to avoid spinning defects,based on which a proper process scheme of hot spinning of TA15 alloy was obtained and the large-diameter and thin-walled cylindrical workpieces were formed with good quality.The results show that spinning temperature has distinct influence on forming quality of spun workpieces.The range of spinning temperature determines the spinnability of titanium alloy and the ununiformity of temperature distribution near the deformation zone leads to the formation of bulge.The reasonable heating method is that the deforming region is heated to the optimum temperature range of 600-700 ℃,the deformed region is heated continuously and a certain length of undeformed region is preheated.With the thickness-to-diameter ratio(t/D) of spun workpiece reducing to certain value(t/D<1%),surface bulge and corrugation is rather easier to come into being,which could be controlled through restraining diameter growth and employing smaller reduction rate and lower temperature in the optimum spinning temperature range. 关键词：TA15 titanium alloy hot SPINNING CYLINDRICAL WORKPIECE FORMING DEFECT thickness-to-diameter ratio

相关文献

参考文献（11）
引证文献（1）
耦合文献（58）

参考文献(11)

引证文献(1)

耦合文献(58)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Hot spinning of cylindrical workpieces of TA15 titanium alloy

参考文献(11)

引证文献(1)

耦合文献(58)

用户提示