High Cr white cast iron/carbon steel bimetal liner by lost foam casting with liquid-liquid composite process

查看全文 作　　者：Xiao [1,2]Xiaofeng;Ye [1]Shengping;[3]YinWeixin;Zhou [1]Xiaoguang;Xue [4]Qiong 高影响力作者 机构地区：[1]State Key Laboratory of Material Processing and Die&Mould Technology,Huazhong University of Science and Technology,Wuhan 430074,China;[2]School of Mechanical Engineering and Automation,Wuhan Textile University,Wuhan 430073,China;[3]Wuhan ZhiKe Abrasive-Resistant Material S&T Development Co.,Ltd,Wuhan 430073,China;[4]College of Science,Wuhan University of Technology,Wuhan 430079,China高影响力机构 出　　处：《China Foundry》索引2012年第9卷第2期,共7页高影响力期刊 基　　金：supported by the National Natural Science Foundation of China under grant No.50805109;the Fundamental Research Funds for the Central Universities under grant No.2011-1a-023 摘　　要：Liners in wet ball mill for mineral processing industry must bear abrasive wear and corrosive wear, and consequently,the service life of the liner made from traditional materials,such as Hadfield steel and alloyed steels,is typically less than ten months.Bimetal liner,made from high Cr white cast iron and carbon steel,has been successfully developed by using liquid-liquid composite lost foam casting process.The microstructure and interface of the composite were analyzed using optical microscope,SEM,EDX and XRD.Micrographs indicate that the boundary of bimetal combination regions is staggered like dogtooth,two liquid metals are not mixed,and the interface presents excellent metallurgical bonding state.After heat treatment,the composite liner specimens have shown excellent properties,including hardness>61 HRC,fracture toughnessα k >16.5 J·cm-2 and bending strength >1,600 MPa.Wear comparison was made between the bimetal composite liner and alloyed steel liner in an industrial hematite ball mill of WISCO,and the results of eight-month test in wet grinding environment have proved that the service life of the bimetal composite liner is three times as long as that of the alloyed steel liner. 关 键 词：bimetal liner liquid-liquid composite process lost foam casting high Cr white cast iron
相关文献

参考文献(12)

引证文献(11)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费