Effects of pretreatment and HVOF sprayed cermet coating on fatigue properties of TC21 titanium alloy

查看全文 作　　者：DU [1]DongXing;LIU [1]DaoXin;MENG [2]BaoLi;ZHANG [1]XiaoHua 高影响力作者 机构地区：[1]College of Aeronautics,Institute of Corrosion and Protection,Northwestern Polytechnical University;[2]Xi'an Aircraft International Corporation高影响力机构 出　　处：《Science China(Technological Sciences)》索引2013年第56卷第4期,共9页高影响力期刊 基　　金：supported by the National Natural Science Foundation of China (Grant Nos. 51171154 and 51101127) 摘　　要：The effects of grit blasting (GB),shot peening (SP) pretreatment and high velocity oxygen fuel(HVOF) sprayed WC-17Co cermet coating on the fatigue properties of the novel ultra-high strength TC21 titanium alloy were investigated with a rotating bending fatigue test machine.The basic properties and surface integrity of the coating were investigated by using X-ray diffraction (XRD),surface roughness meter,microscopic hardness tester,scanning electron microscopy (SEM) and X-ray stress test instruments.The results showed that the residual compressive stress could be introduced into the surface of TC21 alloy by GB and SP pretreatment,and that HVOF sprayed WC-17Co coating was compactly bonded with TC21 alloy substrate and it significantly improved the surface hardness of the substrate.However,there was a certain residual tensile stress in the sublayer of the coating.SP could significantly increase fatigue resistance of TC21 alloy due to the surface residual compressive stress.There was no significant effect on fatigue resistance by GB treatment due to the offset between the influence of surface residual compressive stress and the surface notch effect.The fatigue resistance of TC21 alloy was significantly reduced by HVOF WC-17Co coating prepared with GB pretreatment.This could be attributed to the relaxation of surface residual compressive stress during the HVOF heating process,pore defects and residual tensile stress distribution in the WC-17Co coating with low toughness,and the surface notch induced by GB.The fatigue resistance of TC21 alloy was slightly reduced by HVOF WC-17Co coating prepared with SP pretreatment.This was attributed to the offset between the advantage effect by SP and disadvantageous effect of WC-17Co coating and high temperature factor during the HVOF process. 关 键 词：金属陶瓷涂层 HVOF喷涂 疲劳性能 预处理 钛合金 TC21合金 超音速火焰喷涂 表面粗糙度
相关文献

参考文献(22)

引证文献(4)

耦合文献(22)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费