A general strategy for the reliable joining of Al/Ti dissimilar alloys via ultrasonic assisted friction stir welding

查看全文 作　　者：Zhongwei [1]Ma;Yanye [1]Jin;Shude [1]Ji;Xiangchen [1]Meng;Lin [1]Ma;Qinghua [1]Li

机构地区：[1]School of Aerospace Engineering, Shenyang Aerospace University

出　　处：《Journal of Materials Science & Technology》索引2019年第35卷第1期,共6页

摘　　要：Ultrasonic assisted friction stir welding(UaFSW) was used to join 6061-T6 aluminum and Ti6Al4 V alloys.A small plunge depth endowed with the low heat input was used and the sound joints without obvious thickness reduction were achieved. A diffusion-type bonding without the intermetallic compounds layer was observed at the joint interface. The ultrasonic improved the diffusion thickness and decreased the average size of grains and titanium alloy fragments. A hook-like structure was formed at the bottom interface of the UaFSW joint, which improved the bonding length and the mechanical interlocking. The microhardness of the stir zone was increased because of the further grain refinement induced by ultrasonic. The maximum tensile strength of the UaFSW joint was 236 MPa, which reached 85% of the base6061-T6 alloy. 关键词：FRICTION STIR welding ULTRASONIC Aluminum/titanium alloys Microstructure Mechanical properties

相关文献

参考文献（40）
引证文献（11）
耦合文献（0）

参考文献(40)

引证文献(11)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

A general strategy for the reliable joining of Al/Ti dissimilar alloys via ultrasonic assisted friction stir welding

参考文献(40)

引证文献(11)

用户提示