Microstructure and Tribological Behavior of a TiO_2/hBN Composite Ceramic Coating Formed via Micro-arc Oxidation of Ti–6Al–4V Alloy

查看全文 作　　者：Ni [1]Ao;Daoxin [1]Liu;Shuaixing [1,2]Wang;Qing [2]Zhao;Xiaohua [1]Zhang;Mengmeng [1]Zhang 高影响力作者 机构地区：[1]College of Aeronautics, Institute of Corrosion and Protection, Northwestern Polytechnical University;[2]National Defense Key Discipline Laboratory of Light Alloy Processing Science and Technology, Nanchang Hangkong University高影响力机构 出　　处：《Journal of Materials Science & Technology》索引2016年第32卷第10期,共6页高影响力期刊 基　　金：the Open Foundation of National Defense Key Discipline Laboratory of Light Alloy Processing Science and Technology (Grant No.gf201401001);the National Natural Science Foundation of China (Grant No.51171154) 摘　　要：A composite coating containing hexagonal boron nitride(hBN) particles and titanium oxide(TiO_2) was formed on the surface of Ti–6Al–4V alloy via micro-arc oxidation(MAO). The effect of quantity of the hBN-particles added into electrolyte on microstructure, composition, and wear behavior of the resulting composite coatings was investigated. Microstructure, phase composition, and tribological behavior of the resulting MAO coatings were evaluated via scanning electron microscopy, X-ray diffraction, and ball-on-disc abrasive tests. The results reveal that the TiO_2/hBN composite coating consisting of rutile TiO_2, anatase TiO_2, and an hBN phase was less porous than particle-free coating. Furthermore, the presence of hBN particles in the MAO coating produced an improved anti-friction property. The composite coating produced in the electrolyte containing 2 g/L of hBN particles exhibited the best wear resistance.The outer loose layer of the MAO coatings was removed by a mechanical polishing process, which led to a significant improvement in the wear resistance and anti-friction properties of the MAO coatings and highlighted an essential lubricating role of hBN particles in the composite coatings. However, wear mechanism of the MAO coatings was not relevant to the presence of hBN particles, where fatigue wear dominated the anti-fraction properties of the MAO coatings with and without hBN particles. 关 键 词：陶瓷复合涂层 微观结构 微弧氧化 hBN 纳米TIO2 钛合金 摩擦学性能 六方氮化硼
相关文献

参考文献(25)

引证文献(23)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费