Investigation of Solidification and Segregation Characteristics of Cast Ni-Base Superalloy K417G

查看全文 作　　者：Li [1]Gong;Bo [1]Chen;Zhanhui [1]Du;Mengshu [1]Zhang;Ruichang [1]Liu;Kui [1]Liu

机构地区：[1]Institute of Metal Research, Chinese Academy of Sciences

出　　处：《Journal of Materials Science & Technology》索引2018年第34卷第3期,共10页

摘　　要：Differential scanning calorimetry(DSC) analysis, isothermal solidification experiment and Thermo-Calc simulation were employed to investigate solidification characteristics of K417 G Ni-base superalloy. Electron probe microanalysis(EPMA) was employed to analyze the segregation characteristics. Liquidus,solidus and the formation temperatures of main phases were measured. In the process of solidification,the volume fraction of liquid dropped dramatically in the initial stage, while the dropping rate became very low in the final stage due to severe segregation of positive segregation elements into the residual liquid. The solidification began with the formation of primary γ. Then with solidification proceeding, Ti and Mo were enriched in the liquid interdendrite, which resulted in the precipitation of MC carbides in the interdendrite. Al accumulated into liquid at the initial stage, but gathered to solid later due to the precipitation of γ/γ’ eutectic at the intermediate stage of solidification. However, Co tended to segregate toward the solid phase. In the case of K417 G alloy, combining DSC analysis and isothermal solidification experiment is a good way to investigate the solidification characteristics. Thermo-Calc simulation can serve as reference to investigate K417 G alloy. 关键词：分离特征 Ni 演员计算模拟热量测定 TRON 微量分析形成温度

相关文献

参考文献（28）
引证文献（19）
耦合文献（3）

参考文献(28)

引证文献(19)

耦合文献(3)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Investigation of Solidification and Segregation Characteristics of Cast Ni-Base Superalloy K417G

参考文献(28)

引证文献(19)

耦合文献(3)

用户提示