High-temperature failure mechanism and defect sensitivity of TC17 titanium alloy in high cycle fatigue

查看全文 作　　者：Gen [1]Li;Chengqi [1,2]Sun 高影响力作者 机构地区：[1]State Key Laboratory of Nonlinear Mechanics,Institute of Mechanics,Chinese Academy of Sciences;[2]School of Engineering Science,University of Chinese Academy of Sciences高影响力机构 出　　处：《Journal of Materials Science & Technology》索引2022年第27期,共13页高影响力期刊 基　　金：financially supported by the National Natural Science Foundation of China(No.91860112);the International Postdoctoral Exchange Fellowship Program(China)。 摘　　要：Crack initiation is an essential stage of fatigue process due to its direct effect on fatigue failure.However,for titanium alloys in high-temperature high cycle fatigue(HCF),the crack initiation mechanisms remain unclear and the understanding for the defect sensitivity is also lacking.In this study,a series of fatigue tests and multi-scale microstructure characterizations were conducted to explore the high-temperature failure mechanism,and the coupled effect of temperature and defect on TC17 titanium alloy in HCF.It was found that an oxygen-rich layer(ORL)was produced at specimen surface at elevated temperatures,and brittle fracture of ORL at surface played a critical role for surface crack initiation in HCF.Besides,internal crack initiation with nanograins at high temperatures was a novel finding for the titanium alloy.Based on energy dispersive spectroscopy,electron backscatter diffraction and transmission electron microscope characterizations,the competition between surface and internal crack initiations at high temperatures was related to ORL at surface and dislocation resistance in inner microstructure.The fatigue strengths of smooth specimens decreased at elevated temperatures due to the lower dislocation resistance.While the fatigue strengths of the specimens with defect were not very sensitive to the temperatures.Finally,a fatigue strength model considering the coupled effect of temperature and defect was proposed for TC17titanium alloy. 关 键 词：TC17 titanium alloy High temperature DEFECT High cycle fatigue Oxygen-rich layer Rough area
相关文献

参考文献(43)

引证文献(8)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费