Quality Control:Internal Defects Formation Mechanism of Selective Laser Melting Based on Laser-powder-melt Pool Interaction:A Review

查看全文 作　　者：Guang [1]Yang;Yilian [1]Xie;Shuo [1]Zhao;Lanyun [1]Qin;Xiangming [2]Wang;Bin [2]Wu 高影响力作者 机构地区：[1]School of Mechanical Engineering,Shenyang Aerospace University,Shenyang,110136,China;[2]AVIC Shenyang Aircraft Design and Research Institute,Shenyang,110035,China高影响力机构 出　　处：《Chinese Journal of Mechanical Engineering(Additive Manufacturing Frontiers)》索引2022年第1卷第3期,共21页高影响力期刊 基　　金：National Natural Science Foundation of China(Grant No.51975387). 摘　　要：Selective laser melting(SLM)is a 3D printing technology with a high near-net-shape ability and forming accuracy.However,the inevitable internal defects significantly hinder its development.Therefore,it is essential to fully understand the causes of internal defects in SLM processing and minimize the defects to achieve quality control accordingly.This work reviews the recent studies on internal defects in SLM,presenting the main internal defects of SLM as impurities,lack of fusion,gas pores,and micro-crack.These internal defects occur on the various phenomena in the laser-powder-melt pool(LPMP)stage.The formation of SLM internal defects is mainly affected by oxidation,denudation,balling,spatter,and keyholes;here,balling,spattering,and the keyhole phenomenon are the main factors causing internal defects in LPMP.Hence,this paper focuses on reviewing the balling effect,spatter behavior,and keyhole phenomenon,introducing the action mechanism of the above three phenomena under different process conditions.Additionally,the spatter behavior when forming internal defects is proposed.This review also considers the correlation between the spatter behavior and keyhole phenomenon and makes an important contribution to understanding and reducing SLM internal defects.It presents a reliable opinion on real-time monitoring and machine intelligent learning for SLM processing in the future,as well as supporting a systematic thinking for the suppression of defect formation in SLM. 关 键 词：Selective laser melting Quality control Internal defects Balling effect Spatter behavior Keyhole phenomenon
相关文献

参考文献(153)

引证文献(12)

网站首页 | 关于我们 | 联系我们 | 产品服务 | 客服中心 | 广告服务 | 版权声明 | 网站联盟 | 友情链接 | 售卡网点

版权所有© 渝B2-20050021-1　渝公网安备 50019002500403号　违法和不良信息举报中心

互联网出版许可证 新出网证(渝)字10号 全国400电话 - 免长途话费