3篇
您的检索式：作者名="Benudhar SAHOO"
|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Effect of lanthanum,neodymium on piezoelectric,dielectric and ferroelectric properties of PZT显示文摘The effect of La^(3+)and Nd^(3+)on piezoelectric,dielectric and ferroelectric properties of PZT(Pb(Zr_(0.53)Ti_(0.47))O_(3))was studied.The powders were prepared by“wet-chemical”route followed by calcination at 800℃for 4 h.XRD analysis of the calcined powders confirms the tetragonal phase in the undoped PZT,which gradually decreases with the dopant concentration and the appearance of rhombohedral phase simultaneously.SEM study of sintered pellets reveals the decrease in grain size with the increase in dopant concentration beyond 0.02 mol Nd^(3+)and 0.03 mol La^(3+)respectively.The piezoelectric constant(d_(33))and dielectric properties were maximum for 0.02 mol Nd^(3+)and 0.03 mol La^(3+)respectively.The remnant polarization of La^(3+)-doped sample was higher than Nd^(3+)-doped sample,and the sample with combined dopants shows intermediate remnant polarization(P_(r)).Based on the above study,it is concluded that La^(3+)is more effective than Nd^(3+),including in a mixture of La^(3+)and Nd^(3+)dopants. | Benudhar SAHOO Prasanta Kumar PANDA | 2013 | Journal of Advanced Ceramics2013，2，1： | 6 |
| 2 | Synthesis and characterization of manganese tetroxide(Mn_(3)O_(4))nanofibers by electrospinning technique显示文摘Manganese tetroxide(Mn_(3)O_(4))nanofibers were prepared by electrospinning homogeneous viscous solution of 20 wt%,28 wt%and 36 wt%manganese acetate in poly vinyl alcohol(PVA)and calcining the nanofibers at 1000℃for 2 h.Electrospinning was carried out at 9 kV DC with tip to collector distance(TCD)of 7 cm.Thermo gravimetric analysis(TGA)of the fibers indicates the pure phase of manganese oxide above 500℃.XRD analysis of calcined(at 1000℃)nanofibers indicates the formation of phase-pure tetragonal Mn_(3)O_(4).Scanning electron microscopy(SEM)studies show the fibers cylindrical with the diameters in the range of 100-600 nm and aspect ratio>1000.In general,the average diameter of the green fibers decreases with the increase in manganese acetate concentration.The diameter of calcined nanofibers is reduced by 34%. | Benudhar SAHOO Prasanta Kumar PANDA | 2013 | Journal of Advanced Ceramics2013，2，1： | 2 |
| 3 | Effect of Zr^(4+)on piezoelectric,dielectric and ferroelectric properties of barium calcium titanate lead-free ceramics显示文摘Ba_(0.85)Ca_(0.15)(Ti1−xZrx)O_(3)(BCTZ)ceramics with x=0.05,0.10,_(0.15),0.20,0.25,0.30 were prepared by the solid-state reaction method.Calcination of the powders was carried out at 1100°C for 4 h and the green pellets were sintered at 1400°C for 2 h.X-ray diffraction patterns of the sintered pellets showed tetragonal splitting up to x=0.10 while the mixture of the rhombohedral/cubic phase appeared at higher ZrO_(2)concentrations.Maximum piezoelectric charge constant d33=510 pC/N and strain(S=0.103%)were measured for BCT doped by 0.10 mol ZrO_(2).Dielectric constant,remnant polarization and saturation polarization also found maxima for this composition.The Curie temperature(TC)of the compositions decreased with increase in ZrO_(2)concentration and reached 98°C,87°C and 36°C at x=0.05,0.10,_(0.15)mol,respectively.The remaining compositions have TC below the room temperature;therefore,they can be used for subzero/cryogenic applications.The scanning electron microscopy study revealed an increase in grain size with increase in ZrO_(2)concentration and confirmed the complete solubility of ZrO_(2)in the crystal lattice.Overall,low ZrO_(2)-doped BCT compositions with high d33 could be suitable for low temperature(<80°C)applications. | Prasanta Kumar Panda Benudhar Sahoo V.Sureshkumar Ekaterina Dmitrievna Politova | 2021 | Journal of Advanced Dielectrics2021，11，6： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员