| 1 | Comparative study of Sm^(3+) ions doped phosphate based oxide and oxy-fluoride glasses for solid state lighting applications显示文摘The physical and luminescent properties of Sm^(3+)-doped oxide and oxy-fluoride phosphate glasses were investigated. The glass samples with chemical composition of 69 P_2 O_5-10 BaO-10 ZnO-10 Gd_2 O_3-1 Sm_2 O_3 and 69 P_2 O_5-10 BaO-10 ZnO-10 GdF_3-1 Sm_2 O_3 were prepared by conventional melt quenching technique. The prepared glass samples were characterized with density, molar volume, refractive index,FTIR, UV-Vis-NIR, photo luminesce nce, radio luminescence, decay time profile and CIE diagram. The density and refractive index of the oxide glass have higher values as compared to the oxy-fluoride glass.The FTIR spectra show the reduction of O-H group in oxy-fluoride glass. The characteristic peaks of Sm^(3+)are observed at 360,372,402,438,419,473,944,1077,1227,1373,1474,1529 and 1585 nm in UV-VIS-NIR spectra. These peaks are related respectively to the transitions from ground state ~6 H_(5/2) to ~4 D_(3/2), ~6 P_(7/2),6 P3/2, ~4 I_(11/2), ~6 F_(11/2), ~6 F_(9/2), ~6 F_(7/2),~6 F_(5/2),~6 F_(3/2), ~6 H_(15/2) and ~6 F_(1/2) excited states. From photoluminescence and radio-luminesce nce it is observed that the oxy-fluoride glass samples show better emission intensity than the oxide glass. The Judd-Ofelt theory(J-0 theory) was used to find J-O intensity Ω_λ(λ = 2,4 and 6)parameters and radiative properties such as transition probability, stimulated emission cross section and branching ratios for titled glasses. The trend observed in the J-O parameters is Ω_4 >Ω_2 >Ω_6. The transition probability,emission cross section and branching ratio have the highest values for the ~4 G_(5/2)→~6 H_(7/2)transition. The CIE coordinates of the prepared glass samples are positioned in the orange region and the CCT value is 3776.105 for oxide and oxyfluoride glass. The oxy-fluoride glass has shorter decay time as compared to the oxide glass and it is recorded to be 1.62 and 1.32 ms for oxide and oxy-fluoride respectively. According to the results obtained in this work, it is obvious that these glass samples can be good candidate materials for producing cool orange light. | M.Shoaib G.Rooh R.Rajaramakrishna N.Chanthima N.Kiwsakunkran H.J.Kim J.Kaewkhao S.Tuscharoen | 2019 | Journal of Rare Earths2019，37，4： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员