| 1 | Enhanced dielectric and electrocaloric properties in lead-free rod-like BCZT ceramics显示文摘Ba0.85Ca0.15Zr0.10Ti0.90O3(BCZT)lead-free ceramics demonstrated excellent dielectric,ferroelectric,and piezoelectric properties at the morphotropic phase boundary(MPB).So far,to study the effect of morphological changes on dielectric and ferroelectric properties in lead-free BCZT ceramics,researchers have mostly focused on the influence of spherical grain shape change.In this study,BCZT ceramics with rod-like grains and aspect ratio of about 10 were synthesized by surfactant-assisted solvothermal route.X-ray diffraction(XRD)and selected area electron diffraction(SAED)performed at room temperature confirm the crystallization of pure perovskite with tetragonal symmetry.Scanning electron microscopy(SEM)image showed that BCZT ceramics have kept the 1D rod-like grains with an average aspect ratio of about 4.Rod-like BCZT ceramics exhibit enhanced dielectric ferroelectric(εr=11,906,tanδ=0.014,Pr=6.01μC/cm^2,and Ec=2.46 kV/cm),and electrocaloric properties(ΔT=0.492 K andz=0.289(K×mm)/kV at 17 kV/cm)with respect to spherical BCZT ceramics.Therefore,rod-like BCZT lead-free ceramics have good potential to be used in solid-state refrigeration technology. | Zouhair HANANI Soukaina MERSELMIZ Abdelaadim DANINE Nicolas STEIN Daoud MEZZANE M’barek AMJOUD Mohammed LAHCINI Yaovi GAGOU Matjaz SPREITZER Damjan VENGUST Zdravko KUTNJAK Mimoun El MARSSI Igor ALUK'YANCHUK Mohamed GOUNE | 2020 | Journal of Advanced Ceramics2020，9，2： | 1 |
您所在的机构暂未开通此部分的功能，请联系管理员